Cast in single strand slab caster of steel melt shop. Liquid steel is produced through electric arc furnace-AOD Convertor/VOD-Ladle refining furnace route.

Cast from twin stand bloom caster at Steel Melt Shop. Liquid steel is produced through electric arc furnace-AOD convertor-ladle refining furnace route.

+ Size : 200 mm sq.
+ 260 x 200 mm sq. (on request).

+ HR Black : As cast/ ground slabs are first heated and soaked in reheating furnace, rolled in roughing mill to intermediate thickness and then to the final thickness in the steckel mill.
+ HRAP : Hot Rolled coils are annealed & pickled in continuous Annealing-Pickling lines having scale breaker, shot blasting unit, Electrolytic Sulphuric Acid and Mixed Acid bath.
HRAP coils have a cleaner surface & have improved mechanical properties for downstream processing.

Our cold rolling facility is equipped with all state-of-art facilities like 20-Hi-Sendzimier cold rolling mill with IMR Shifting, Mill Tilting and Shape meter advantages for higher degree of Shape & profile correction. The CR Annealing & Pickling line is on environment friendly LPG fuel with better and fastest temperature control associated with Electrolytic and Acid Pickling with very high control of pickling process. The online Skin Pass and Tension Leveling has made this line capable of producing finished 2B/2D product at par with international quality. The on-line automatic surface inspection system also provides a very high resolution surface quality. There is provision of offline Skin Pass Mills which helps to cater high luster requirements also. Other facilities include Bright Annealing units (under commissioning phase) in cracked ammonia atmosphere and Strip Grinding line to produce desired surface finishes.

No1 finish plates are produced after annealing and pickling or by cutting hot rolled annealed pickled coils to desired lengths.